HEX HEAD BOLT 7/16-14 X 3 NC GR5 BLACK (VR275/BT50) - 073-545
INF103121N
Prix régulier
$1.66
Preorder today
- Papco® Grade 5 assembly screws, identified by the three radial bar heads marking, are made of medium carbon steel, hardened and tempered for higher tensile strength and holding power.
- Double heat treatment
- Hardened and tempered medium carbon steel: c: 0.28 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure consisting of approximately 90% martensite in the web of the threaded sections of the fasteners after hardening and quenching, and before tempering.
- Papco® Grade 5 assembly screws, identified by the three radial bar heads marking, are made of medium carbon steel, hardened and tempered for higher tensile strength and holding power.
- Double heat treatment
- Hardened and tempered medium carbon steel: c: 0.28 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure consisting of approximately 90% martensite in the web of the threaded sections of the fasteners after hardening and quenching, and before tempering.
INF103121N
Prix régulier
$1.66
Preorder today
- Papco® Grade 5 assembly screws, identified by the three radial bar heads marking, are made of medium carbon steel, hardened and tempered for higher tensile strength and holding power.
- Double heat treatment
- Hardened and tempered medium carbon steel: c: 0.28 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure consisting of approximately 90% martensite in the web of the threaded sections of the fasteners after hardening and quenching, and before tempering.
- Papco® Grade 5 assembly screws, identified by the three radial bar heads marking, are made of medium carbon steel, hardened and tempered for higher tensile strength and holding power.
- Double heat treatment
- Hardened and tempered medium carbon steel: c: 0.28 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure consisting of approximately 90% martensite in the web of the threaded sections of the fasteners after hardening and quenching, and before tempering.