HEX HEAD BOLT 1-14 X 9 NF GR8 BLACK (VR15) - B078-822
INF106331N
Prix régulier
$30.05
Ready to ship (13)
- Polished and beveled claws for precise penetration
- Six radial bars
- Double heat treatment
- Use with grade 8 nuts to develop the full strength of the cap screw
- Hardened and tempered medium carbon steel: c: 0.25 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure composed of approximately 90% martensite in the core of the threaded sections of the fasteners after hardening and quenching, and before tempering.
- Polished and beveled claws for precise penetration
- Six radial bars
- Double heat treatment
- Use with grade 8 nuts to develop the full strength of the cap screw
- Hardened and tempered medium carbon steel: c: 0.25 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure composed of approximately 90% martensite in the core of the threaded sections of the fasteners after hardening and quenching, and before tempering.
INF106331N
Prix régulier
$30.05
Ready to ship (13)
- Polished and beveled claws for precise penetration
- Six radial bars
- Double heat treatment
- Use with grade 8 nuts to develop the full strength of the cap screw
- Hardened and tempered medium carbon steel: c: 0.25 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure composed of approximately 90% martensite in the core of the threaded sections of the fasteners after hardening and quenching, and before tempering.
- Polished and beveled claws for precise penetration
- Six radial bars
- Double heat treatment
- Use with grade 8 nuts to develop the full strength of the cap screw
- Hardened and tempered medium carbon steel: c: 0.25 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure composed of approximately 90% martensite in the core of the threaded sections of the fasteners after hardening and quenching, and before tempering.