HEXAGONAL HEAD BOLT 9/16-12 X 1 3/4 NC GR8 BLACK (VR250/BT25) - 077-629
INF105189N
Prix régulier
$2.58
Preorder today
- The satin finish offers corrosion resistance and a non-slip grip.
- Six radial bars
- Double heat treatment
- Use with grade 8 nuts to develop the full strength of the cap screw
- Hardened and tempered medium carbon steel: c: 0.25 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure composed of approximately 90% martensite in the core of the threaded sections of the fasteners after hardening and quenching, and before tempering.
- The satin finish offers corrosion resistance and a non-slip grip.
- Six radial bars
- Double heat treatment
- Use with grade 8 nuts to develop the full strength of the cap screw
- Hardened and tempered medium carbon steel: c: 0.25 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure composed of approximately 90% martensite in the core of the threaded sections of the fasteners after hardening and quenching, and before tempering.
INF105189N
Prix régulier
$2.58
Preorder today
- The satin finish offers corrosion resistance and a non-slip grip.
- Six radial bars
- Double heat treatment
- Use with grade 8 nuts to develop the full strength of the cap screw
- Hardened and tempered medium carbon steel: c: 0.25 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure composed of approximately 90% martensite in the core of the threaded sections of the fasteners after hardening and quenching, and before tempering.
- The satin finish offers corrosion resistance and a non-slip grip.
- Six radial bars
- Double heat treatment
- Use with grade 8 nuts to develop the full strength of the cap screw
- Hardened and tempered medium carbon steel: c: 0.25 to 0.55, p: 0.025 maximum, s: 0.025 maximum
- For dowels only, the sulfur content may be a maximum of 0.13%
- Sufficient hardenability is required to ensure a microstructure composed of approximately 90% martensite in the core of the threaded sections of the fasteners after hardening and quenching, and before tempering.