NORDBAK HIGH TEMPERATURE WEAR COMPOUND 25 LB. NET WT. SET - 235631 - 235631
LOC99112
Prix régulier
$1,255.89
Preorder today
- Resistant to abrasion from sliding and temperatures up to 450°F
- Must be post-cured for maximum temperature resistance and performance.
- 4:1, 3.9: mixing ratio of 1:1
- 30 minutes of work life
- Compressive strength of 15,000 lb/in²
- D 90 Shore hardness
- > 199.4 flash point deg. F point of part a and 249.8 flash point deg. F point of part b
- 2.3337 specific severity of parts a and 1.7911 specific severity of part b
- Resistant to abrasion from sliding and temperatures up to 450°F
- Must be post-cured for maximum temperature resistance and performance.
- 4:1, 3.9: mixing ratio of 1:1
- 30 minutes of work life
- Compressive strength of 15,000 lb/in²
- D 90 Shore hardness
- > 199.4 flash point deg. F point of part a and 249.8 flash point deg. F point of part b
- 2.3337 specific severity of parts a and 1.7911 specific severity of part b
LOC99112
Prix régulier
$1,255.89
Preorder today
- Resistant to abrasion from sliding and temperatures up to 450°F
- Must be post-cured for maximum temperature resistance and performance.
- 4:1, 3.9: mixing ratio of 1:1
- 30 minutes of work life
- Compressive strength of 15,000 lb/in²
- D 90 Shore hardness
- > 199.4 flash point deg. F point of part a and 249.8 flash point deg. F point of part b
- 2.3337 specific severity of parts a and 1.7911 specific severity of part b
- Resistant to abrasion from sliding and temperatures up to 450°F
- Must be post-cured for maximum temperature resistance and performance.
- 4:1, 3.9: mixing ratio of 1:1
- 30 minutes of work life
- Compressive strength of 15,000 lb/in²
- D 90 Shore hardness
- > 199.4 flash point deg. F point of part a and 249.8 flash point deg. F point of part b
- 2.3337 specific severity of parts a and 1.7911 specific severity of part b